NYLON-6 DIPPED TYRE CORD FABRICS
CORD CONSTRUCTION |
840D/1 |
1050D/1 |
1260D/1 |
1680D/1 |
840D/2 |
1260D/2 |
1260D/3 |
1680D/2 |
1890D/2 |
TENSILE STRENGTH
N/end min. |
67 |
86 |
98 |
127 |
132.3 |
205.8 |
303.8 |
269.5 |
303.8 |
ELONGATION %
AT 22.5N
AT 33.3N
AT 44.1N
AT 66.6N
AT 88.2N
AT 100N
|
7.5±1.0
|
7.5±1.0
|
7.0±1.0
|
8.0±1.0 |
9.5±0.8 |
9.5±0.5 |
9.5±0.8 |
9.5±0.8 |
9.5±0.8 |
ADHESION
(H-TEST) N/CM min. |
49 |
65 |
64 |
78 |
107.8 |
137.2 |
166.6 |
156.8 |
166.6 |
CORD
GAUGE MM |
0.32±0.03 |
0.36±0.03 |
0.43±0.03 |
0.50±0.03 |
0.55±0.04 |
0.65±0.04 |
0.78±0.04 |
0.75±0.03 |
0.78±0.04 |
TWIST T/10cm |
21±1.5 |
19±1.0 |
19±1.0 |
16±1.0 |
46±1.5/
46±1.5 |
37±1.5/
37±1.5 |
32±1.5/
32±1.5 |
33±1.5/
32±1.5 |
32±1.5/
32±1.5 |
DIP PICK UP % |
4.2±1.2 |
4.2±1.0 |
4.2±1.2 |
4.2±1.2 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
ELONGATION AT BREAK % |
20±2 |
20±2 |
20±2 |
20±2 |
22±2 |
23±2 |
23±2 |
23±2 |
23±2 |
MOISTURE
% max |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
HEAT SHRINKAGE
(in hot air 150℃×30min.)
% max |
4 |
4 |
4 |
4 |
6.5 |
6.5 |
6.5 |
6.5 |
6.5 |
REMARKS:
FABRIC WIDTH, ROLL LENGTH, EPI, TENSILE STRENGTH, ADHESION AND TWIST CAN BE ADJUSTED ACCORDING TO CLIENT’S REQUEST.
| |
|